Hydrogen Annealing
- 650oC, 60 sec anneal in H2/Ar significantly improves CV “stretch out”
(caused by elevated Dit), decreases hysteresis (caused by positive oxide
charge) and VFB (also caused by positive oxide charge)
- no significant changes seen in leakage or capacitance
- NOTE: Hg probe overestimates DVFB